Influence of surface treatments on the bond strength of metal brackets to CAD/CAM materials and discoloration after various refinishing procedures
Scanning electron microscopy and atomic force microscopy study
verfasst von:
Murat Tunca, Beyza Unalan Degirmenci
Erschienen in:
Journal of Orofacial Orthopedics / Fortschritte der Kieferorthopädie
|
Sonderheft 3/2023
Einloggen, um Zugang zu erhalten
Abstract
Purpose
This study evaluated the shear bond strength (SBS) of a metal bracket bonded to three different computer-aided design/computer-aided manufacturing (CAD/CAM) restoration materials pretreated with different surface treatments. In addition, the surface topography and color change of the restorations after debonding with two different tungsten carbide burs were examined.
Methods
A total of 216 plates were cut from three different CAD/CAM blocks, each of which was divided into three subgroups with different pretreatment methods: (1) acid etching, (2) sandblasting, and (3) laser irradiation. Incisor metal brackets were bonded. The SBS test was performed, and the failure types were classified. Then, samples were randomly divided into two subgroups according to the adhesive removal procedure to be used: a tungsten carbide bur with 12 blades or 24 blades (n = 12). Color change was calculated based on the ∆E00, and surface morphology was evaluated via SEM and AFM analysis.
Results
The SBS data revealed that the type of CAD/CAM material and the applied surface treatment significantly affected bond strength. The highest SBS values were detected for the Grandio Blocs (VOCO GmbH, Cuxhaven, Germany; 14.3 ± 4.4 MPa), and the lowest was observed for Cerasmart (GC Europe, Leuven, Belgium; 12.0 ± 4.0 MPa). The ∆E00 results demonstrated significant differences only as a result of the applied surface treatment. The ∆E00 value in all groups was above the 1.77 threshold.
Conclusion
CAD/CAM material types and surface treatments affected the bond strength, but the interactions of these factors did not. The chosen surface treatment also significantly affected the ∆E00 after the polishing was done.